Alloy Grade UNS: HX – Hot Gas Corrosion Resistance

  • Overview

    For severe hot gas corrosion resistance at higher temperatures. Service limit 980 degrees Celsius (1800 degrees Fahrenheit).

  • Typical Uses

    Carburizing boxes, hearth plates, heat treatment and calciner components, muffles, retorts, roller hearths.

  • MetalTek Grade

    MTEK 15-65

Similar Specifications

Cast UNS: N06006

Cast Grade: HX

Cast ASTM: A297

Typical Chemical Composition (% by wt.)

Aluminum: n/a

Carbon: 0.35-0.75

Chromium: 15-19

Manganese: 2

Iron: n/a

Copper: n/a

Nickel: 64-68

Lead: n/a

Tin: n/a

Silicon: 2.5

Zinc: n/a

Minimum Mechanical Properties

Tensile, ksi

0

Tensile, MPa

0

Heat Treatment: Not Heat Treated

Explore Other Alloys

Gears

Non-Ferrous

Non-ferrous alloys are, literally, materials that are not iron-based. While others may provide non-ferrous materials of other materials, the MetalTek family of non-ferrous alloys are copper-based. In general, these materials deliver high strength, and excellent wear and corrosion resistance. They are often found in marine applications and also bushing, bearing, and gear environments.
Stainless Steel Parts

Stainless Steel

Stainless steels owe their ability to resist corrosion primarily to the presence of a passive film on their surface. Chromium is chiefly responsible for formation of the passive film. Iron ceases to rust at approximately 12% chromium content and resistance to oxidizing corrosives increases rapidly with chromium content up to approximately 20%.
Petrochemical Fittings

Specialty Alloys

Specialty Alloys comprise a broad group of materials that deliver properties for more demanding applications, use more exotic or expensive materials, or require special processes to manufacture. Where standard materials may not offer desired performance, specialty alloys (including those that are modified further) may be a sensible selection.