Alloy Grade UNS: J91631 – “400” Series Material

  • Overview

    J91631 is a "400" series material with high strength and corrosion resistance. This series of metal alloys tend to have better hardness than the 300 series.This stainless steel alloy contains up to 14% chromium and 2.2% nickel.

  • Typical Uses

    Aerospace, bearings, bushings, chemical and food processing equipment, conveyor rollers, cutlery, impellers, medical devices, pump and valve components, turbine engine parts. 

  • MetalTek Grade

    MTEK CA20NW

Similar Specifications

Cast UNS: J91631

Wrought UNS: S41800

Wrought Grade: Greek Ascoloy®

Cast Grade:

Military/AMS: AMS 5354

* AMS specifying investment casting.

Typical Chemical Composition (% by wt.)

Aluminum: n/a

Carbon: 0.15-0.20

Chromium: 12.0-14.0

Manganese: 1

Iron: BAL

Copper: n/a

Nickel: 1.8-2.2

Lead: n/a

Tin: n/a

Silicon: 1

Zinc: n/a

Other: W 2.5-3.5; Mo 0.50 MAX

Minimum Mechanical Properties

Brinell Typical:

0

Tensile, ksi

0

Tensile, MPa

0

Yield, ksi

0

Yield, MPa

0

Elongation

0%

Heat Treatment: Anneal, Harden And Temper

NOTES: Brinell value is MAX.

Explore Other Alloys

Gears

Non-Ferrous

Non-ferrous alloys are, literally, materials that are not iron-based. While others may provide non-ferrous materials of other materials, the MetalTek family of non-ferrous alloys are copper-based. In general, these materials deliver high strength, and excellent wear and corrosion resistance. They are often found in marine applications and also bushing, bearing, and gear environments.
Stainless Steel Parts

Stainless Steel

Stainless steels owe their ability to resist corrosion primarily to the presence of a passive film on their surface. Chromium is chiefly responsible for formation of the passive film. Iron ceases to rust at approximately 12% chromium content and resistance to oxidizing corrosives increases rapidly with chromium content up to approximately 20%.
Petrochemical Fittings

Specialty Alloys

Specialty Alloys comprise a broad group of materials that deliver properties for more demanding applications, use more exotic or expensive materials, or require special processes to manufacture. Where standard materials may not offer desired performance, specialty alloys (including those that are modified further) may be a sensible selection.